Titanium has plasticity, the elongation of purity titanium can be up to 50-60%, and the reduction of area can be up to 70-80%. That makes the production of titanium capillary tube. Forging and rolling the secondary melting titanium ingots into the tube billets, then stretch the tube billet for several times until the titanium capillary tube formed. Due to the good compatibility with human body and corrosion resistance, titanium capillary tube is widely used in the medical industry, including the human body implants, medical equipment internal precision parts, etc.
Seamless tantalum tube is to tantalum ingot after the breakdown of extrusion manufacturing into the pipe, and then to annealing treatment, then after a lot of rolling and annealing finally produce the customer needs to tantalum tube, uniform in all parts of the process pipe performance, mainly produces small specification pipe and capillary materials, applicable to the production of various specifications of products
Welding of tantalum tube is to choose high quality, appropriate size of the tantalum sheet to roll, welding, and then the joint treatment on welds, finally the whole round handle, make suitable size of tantalum tube. This process in the production of tantalum tube wall thickness, the inner surface of good quality and high production efficiency, cost is lower, the most important thing is that can produce large diameter of tantalum tube.
Chemical composition
Composition (%) | |||||||||||||
Grade | Main elements | Impurity content (≤) | |||||||||||
Ta | Nb | Fe | Si | Ni | W | Mo | Ti | Nb | O | C | H | N | |
Ta1 | Bal | — | 0.005 | 0.005 | 0.002 | 0.01 | 0.01 | 0.002 | 0.03 | 0.015 | 0.01 | 0.0015 | 0.005 |
Ta2 | Bal | — | 0.03 | 0.02 | 0.005 | 0.04 | 0.03 | 0.005 | 0.1 | 0.02 | 0.01 | 0.0015 | 0.005 |
TaNb3 | Bal | 1.5~3.5 | 0.03 | 0.03 | 0.005 | 0.04 | 0.03 | 0.005 | — | 0.02 | 0.01 | 0.005 | 0.01 |
TaNb20 | Bal | 17.0~23.0 | 0.03 | 0.03 | 0.005 | 0.04 | 0.03 | 0.005 | — | 0.02 | 0.01 | 0.005 | 0.01 |
TaNb40 | Bal | 35.0~42.0 | 0.01 | 0.005 | 0.01 | 0.05 | 0.02 | 0.01 | — | 0.02 | 0.01 | 0.015 | 0.01 |
Ta2.5W | Bal | — | 0.01 | 0.005 | 0.01 | 2.0 ~ 3.5 | 0.01 | 0.002 | 0.1 | 0.01 | 0.01 | 0.0015 | 0.01 |
Ta10W | Bal | — | 0.01 | 0.005 | 0.01 | 9.0 ~ 11.0 | 0.01 | 0.002 | 0.1 | 0.015 | 0.01 | 0.0015 | 0.01 |
Mechanical properties (Annealed)
UNS No | Tensile strength Min (MPa) | Yield strength Min (MPa) | Elongation Min (%) (25.4mm Gage) |
R05200, R05400 | 207 | 138 | 25 |
R05252 | 276 | 193 | 20 |
R05255 | 481 | 414 | 15 |
R05240 | 276 | 193 | 20 |
TaNb3, TaNb20, the mechanical properties according to the factory measured. |
Tolerance (mm)
OD | OD Tolerance | WT Tolerance |
1~20 | 0.01 | ±5% |
20~25 | 0.05 | ±5% |
25~40 | 0.10 | ±5% |
40~60 | 0.15 | ±5% |
60~80 | 0.20 | ±5% |
80~150 | 0.25 | ±5% |
titanium tube mill | titanium tube in stock |
titanium tube mills | titanium tube inspection method |
titanium tube montreal | titanium tube malaysia |
titanium tube offcuts | titanium tube manufacturer europe |
titanium tube online | titanium tube manufacturer india |
titanium tube pellet smoker 18 | titanium tube manufacturers in japan |
titanium tube perth | titanium tube manufacturers in usa |
titanium tube philippines | titanium tube manufacturers korea |