1045 is a medium tensile carbon steel supplied in the cold drawn or turned, precision ground, polished, chrome plated and final polished condition, with a typical base metal tensile strength of 670 - 800 Mpa, plus a typical hard chrome plated surface hardness of HV 1000 - 1150. Characterised by an extremely smooth surface finish with excellent wear and corrosion resistance, coupled with a base material giving good strength and impact properties, plus good machinability and reasonable weldability.
1045 hard chrome plated bar is used extensively by the hydraulic and pneumatic industries, and is employed by other industry sectors for a wide range of applications.
Typical applications are: Agricultural Equipment, Compressors, Car Jacks and other Transport Lifting equipment, Food Processing Equipment, Hoists, Mining and other Earth Moving Equipment, Machine Tools, Mechanical Tools and Equipment, Rods and Shafts (Various), Waste Disposal Transport and Equipment etc.
Machining
1045 hard chrome plated bar has very good machinability, similar to 1045 uncoated bar. Machining however should commence beneath the chrome plating, or at the unchromed surface at the end of the bar. To protect the polished chrome surface, soft materials such as copper, aluminium or mild steel should be used as clamping materials and any particles of hard chrome should be removed immediately to avoid scratching. Otherwise all machining operations may be carried out satisfactorily.
Welding
1045 hard chrome plated bar is readily weldable (similar to 1045 uncoated bar) providing the correct procedure is employed. The cardboard tube protecting the chrome plating should first be removed from the heat affected area otherwise it can cause some corrosion of the plating due to fumes emitted.
Welding Procedure
Welding of 1045 should always be carried out using low hydrogen electrodes - please consult your welding consumables supplier.
Related Specifications | |
Australia | AS 1443 - 1994 1045 |
Germany | W.Nr 1.0503 C45 |
Great Britain | BS970 - Part 3 - 1991 080A47 |
Japan | JIS G 4051 S45C |
USA | AISI C1045 |
Chemical Composition | ||
Min. % | Max. % | |
Carbon | 0.43 | 0.50 |
Silicon | 0.10 | 0.35 |
Manganese | 0.60 | 0.90 |
Phosphorous | 0 | 0.04 |
Sulphur | 0 | 0.04 |
Typical (Base Metal) Mechanical Properties - As Supplied Condition | ||
Manufacturing Process | Cold Drawn | Turned |
Tensile Strength Mpa | 800 | 670 |
Yield Strength Mpa | 700 | 470 |
Elongation in 50mm % | 9 | 20 |
Hardness Brinell HB | 230 | 200 |
We are a well known worldwide exporter of 304 Stainless Steel Pipes and Tubes Qatar, Ireland, Portugal, Gambia, Thailand, Ukraine, United Kingdom, Netherlands, South Africa, Spain, Turkey, Italy, Libya, Romania, Puerto Rico, Azerbaijan, United Arab Emirates, Pakistan, Philippines, Ghana, Slovakia, Germany, Saudi Arabia, Afghanistan, China, Bolivia, Switzerland, Bangladesh, Taiwan, Oman, Egypt, Greece, Norway, Singapore, Bulgaria, Estonia, Belgium, Yemen, Hong Kong, Ecuador, Sri Lanka, Nepal, Belarus, Finland, Gabon, Iran, Canada, Argentina, Lebanon, Denmark, Trinidad & Tobago,Tunisia, Zimbabwe, United States, Russia, South Korea, Poland, Israel, Australia, Tibet, Kenya, Iran, Austria, Brazil, Hungary, Vietnam, Jordan, Nigeria, Mexico, Croatia, Bhutan, India, New Zealand, Czech Republic, Angola, Algeria, Poland, Kuwait, Mongolia, Sweden, Indonesia, Kazakhstan, Malaysia, Peru, Chile, France, Mexico, Chile, Iraq, Morocco, Colombia, Venezuela, Macau, Bahrain, Lithuania, Nigeria, Costa Rica, Japan, Serbia, Namibia.