Hot Rolled Steel Tee Bar Advantages
Hot rolled steel tee's “T” shape makes it favorable for applications where extensive loading bearing capabilities are a must. The top (Flange) provides compressive stress resistance while the vertical section (web) resists shear and bending. Steel tee bar is also easy to weld, cut, form, and machine. Additional structural steel tee advantages include:
1, High strength
2, Increased durability
3, Good ductility
4, Cost-effective
5, Tough
6, Easy-to-produce
Hot Rolled Steel T-Bar Applications
Once formed, hot rolled steel tee bar provides a cost-effective solution for your structural T-bar needs. However, the cooling process can leave the final product slightly uneven and smaller than during the initial forming process. These processes make hot rolled steel tee bar ideal for heavy-duty industrial applications.
1, General fabrication
2, Manufacturing
3, Repairs
4, Frames
5, Trailers
6, Bridges
7, Mining
8, Material handling
| Imperial | Metric |
Density | 0.282 lb/in3 | 7.8 g/cc |
Ultimate Tensile Strength | 58,000 psi | 400 MPa |
Yield Tensile Strength | 47,700 psi | 315 MPa |
Shear Strength | 43,500 psi | 300 MPa |
Melting Point | 2,590 - 2,670°F | 1,420 - 1,460°C |