1, Low carbon content eliminates carbon precipitation in the welding process
2, Can be used in severe corrosive environments
3, Weld annealing only required in high stress applications
4, Very similar to Type 304
304 & 304L plate and pipes have similar properties and in certain cases are stocked with Dual Certification, where it is concluded that each item has properties and a composition which comply with both steel types. Grade 304H cannot be included in this equation due to the steel’s higher carbon content which is intended for use in elevated temperature applications.
DESCRIPTION | TYPE 304L |
Proof Stress 0.2% (MPa) | 170 |
Tensile strength (MPa) | 485 |
Elongation A5 (%) | 40 |
Hardness | HB: 201 |
UNS No | S30403 |
EN | 1.4301 |
AISI | 304 |
Carbon (C) | 0.03 |
Silicon (Si) | 0.75 |
Manganese (Mn) | 2.00 |
Phosphorus (P) | 0.045 |
Sulphur (S) | 0.030 |
Chromium (Cr) | 18.00 – 20.00 |
Molybdenum (Mo) |
|
Nickel (Ni) | 8.00 – 12.00 |
Nitrogen (N) | 0.10 |
302 stainless steel pipe | 314 stainless steel pipe |
304 seamless stainless steel pipe | 316 stainless steel pipe manufacturer |
304 stainless steel 3 inch pipe | 316 stainless steel pipe suppliers |
304 stainless steel pipe supplier | 316 stainless steel seamless pipe |
304 stainless steel pipe suppliers | 316h stainless steel pipe |
304 stainless steel seamless pipe | 316l stainless steel pipe supplier |
321 stainless steel pipe | 317 stainless steel pipe |
321 stainless steel pipe supplier | 410 stainless steel pipe |